Coated metal substrate

ABSTRACT

A coated metal substrate useful for carrying an exhaust emission treatment catalyst such as a three-way conversion catalyst for use with small engine platforms. The coated metal substrate comprises a metal such as a stainless steel, a carbon steel, a FeCr alloy, Hastelloy and the like. The coating on the metal substrate comprises an alumina silicate having alumina particles impregnated therein. The coating is applied using a liquid dispersion containing an aluminum silicate and the alumina particles are dispersed into the aluminum silicate coating while the coating is still wet. The coated metal substrate is then calcined. Thereafter, a washcoat containing an engine exhaust treatment catalyst may be applied to the surface of the coated metal substrate.

FIELD OF THE INVENTION

The invention relates to a coated metal substrate useful for carrying an engine exhaust treatment catalyst.

BACKGROUND OF THE INVENTION

Small internal combustion engines, especially two-stroke and four-stroke spark ignition engines, are used to provide power to a variety of machinery, e.g., gasoline-powered lawn mowers, chain saws, leaf blowers, string cutters, leaf blowers, motor scooters, motorcycles and the like. Such engines provide a severe environment for a catalytic exhaust treatment apparatus. This is due to the fact that in small engines, the exhaust gas contains a high concentration of unburned fuel and unconsumed oxygen.

Additionally, the vibrational force in a two-stroke engine can be three or four times that of a four-stroke engine. For example, vibrational accelerations of 70 to 90 gravitational acceleration at 150 Hertz have been reported for small internal combustion engines. The harsh vibration and exhaust gas temperature conditions associated with small internal combustion engines lead to several modes of failure in the exhaust gas catalytic treatment apparatus, including failure of the mounting structure by which a catalyst member is secured in the apparatus and consequential damage or destruction of the catalyst member due to the mechanical vibration and to flow fluctuation of the exhaust gas under high temperature conditions.

The catalyst member usually comprises a ceramic-like carrier member typically made of e.g., cordierite, mullite, etc., on which an exhaust treatment catalytic material is coated. The ceramic-like material is subject to cracking and pulverization due to excessive vibration. Metal carrier members, i.e., metal substrates, are obvious replacements for the ceramic-like materials, but have their own problems as brought out below.

In the near future, small internal combustion engines will become subject to stringent federal and state emission control regulations. Accordingly, these small engines will require exhaust emission control systems analogous to those currently employed for control of automotive emissions.

For the exhaust emission control systems to be used for the small internal combustion engines typically a metal substrate (also referred to in the prior art as a metal carrier member) will be coated with an exhaust control treatment catalyst such as a three-way conversion (“TWC”) catalyst that will control the emissions of hydrocarbons, carbon monoxide and nitrogen oxides. The challenge has been to impart the required physical properties to the metal substrate that will permit the catalyst to withstand high temperature conditions with severe vibration and poisons from oil and ash over a wide variety of small engine platforms with limited lives and the need for such small engine platforms to operate under a wide range of air/fuel ratios and space velocities. Major differences in the coefficients of thermal expansion of a precious metal catalyst and the metal substrate exacerbate this problem.

The exhaust control emission catalyst materials are typically used in particulate form with particles in the micron-sized range, e.g., 10 to 20 microns in diameter, so that they can be formed into a slurry and applied as a washcoat on the carrier member. Known TWC catalysts that exhibit good activity and long life comprise one or more platinum group metals (e.g., platinum or palladium, rhodium, ruthenium and iridium) disposed on a high surface area, refractory oxide support, e.g., a high surface area alumina coating. The principal problem associated: with the coating of metal substrates with an exhaust emission control treatment catalyst such as a TWC catalyst is adherence of the catalyst to the metal substrate over the wide range of conditions to which the catalyst-coated metal substrate will be exposed during operation of the small engine platform.

OBJECT OF THE INVENTION

It is an object of the invention to provide a coating composition and a method for coating a metal substrate that is effective for anchoring an exhaust emission control treatment catalyst to the metal substrate.

SUMMARY OF THE INVENTION

The invention relates to a coated metal substrate for use in the catalytic reduction of engine exhaust emissions comprising a metal substrate and an alumina-silicate coating on the metal substrate, said coating having alumina particles dispersed therein.

DETAILS OF THE INVENTION

For the purposes of the present invention, the metal substrate may be comprised of a metal such as stainless steel, a carbon steel, titanium, a FeCr alloy or Hastelloy. Hastelloy is a non-trademarked alloy whose major components are nickel-chromium and molybdenum and containing minor components comprising cobalt, iron and tungsten.

Typically, the metal substrates to be used for the small engine platforms will be present in the form of an expansion cone or exhaust gas silencer, having a length of about 100 to about 300 mm, a diameter ranging from about 30 to about 100 mm, a thickness of about 0.5 to about 3 mm and an inside surface area of about 0.03 to about 0.06m².

The bond coat on the surface of the metal substrate comprises an alumina-silicate composition that contains alumina particles dispersed therein. It has been found that an alumina-silicate composition adheres very well to the surface of the metal substrate. However, the surface of the alumina-silicate bond coat is quite smooth and exhaust emission treatment catalyst compositions do not adhere too well to the surface of the bond coat, particularly under the conditions to which the coated metal substrate will be exposed during operation of the small engine platform. It was found that when particles of alumina were dispersed in the bond coat while it was still wet, after calcination of the resultant coated metal substrate, the exhaust emission treatment catalyst adhered quite well to the coated metal substrate under all operating conditions associated with the small engine platforms.

The procedure for applying the bond coat and for dispersal of the alumina particles in the bond coat is relatively simple. If necessary, the metal substrate is sandblasted to form a rough surface and remove any unwanted particles; thereafter, the sandblasted metal substrate may be washed in 30% acetic acid followed by a water rinse. The bond coat composition comprising an aqueous dispersion in which the major component is an aluminum silicate is then applied to the clean surface of the metal substrate, e.g., by dipping, brushing, sponge roller, air gun spraying, etc. Thereafter, alumina particles are applied, e.g., by dipping, brushing, etc., to the coated metal substrate while the bond coat on the metal substrate is still wet. Loose alumina particles may then be removed from the coated surface, e.g., by a gentle stream of air, by tapping on a hard surface, etc., and the resultant coated metal substrate is thereafter calcined. Subsequent to calcination, an exhaust emission treatment catalytic washcoat containing one or more precious metals such as platinum, palladium, rhodium, etc., may then be applied to the surface of the coated metal substrate by conventional methods well known in the prior art followed by drying and calcination of the catalyst-loaded coated metal substrate.

The process for preparing the coated metal substrate of the invention may be summarized as involving the following steps:

-   -   (a) coating a metal substrate with a liquid dispersion         containing an aluminum silicate;     -   (b) impregnating the coated metal substrate resulting from         step (a) with alumina particles, while the aluminum silicate         coating on the metal substrate is still wet; and     -   (c) calcining the coated metal substrate resulting from step         (b).

Liquid dispersions containing an aluminum silicate are well known in the prior art and are commercially available. A suitable aluminum silicate dispersion is the following composition: component amount, wt. % sodium potassium aluminum silicate about 40 to about 45 water about 35 to about 40 acrylic copolymer about 1 to about 5 chromia titania frit about 1 to about 5 aluminum oxide about 1 to about 5 potassium hydroxide about 1 to about 5 amorphous silica about 1 to about 5 cobalt oxide about 1 to about 5

Another suitable aluminum silicate dispersion is the following composition: component amount, wt. % silicon carbide about 45 to about 50 water about 20 to about 26 aluminum phosphate about 10 to about 15 amorphous silicon oxide binders about 2 to about 6 boric acid about 1 to about 3 ethyl alcohol about 3 to about 7 mullite about 4 to about 6

The alumina particles are applied in step (b) of the process in the form of a powder wherein the particles have a particle size in the range of about 5 to about 15 microns, preferably 6 to 9 microns. The alumina particles are applied in an amount of about 0.01 to about 0.5 g/in² of the aluminum silicate coating that was applied in step (a) of the process. Step (c), i.e., the calcination, is carried out at a temperature of about 350 to about 550° C. for about 0.25 to about 2 hours.

A washcoat containing an engine exhaust treatment catalyst may then be applied (e.g., by spraying, dipping, rolling, etc.) to the coated metal substrate resulting from step (c), followed by air drying at about 60 to about 100° C. for about 0.5 to about 2 hours and subsequent calcination at a temperature of about 350 to about 550° C. for about 0.25 to about 2 hours.

The following nonlimiting examples shall serve to illustrate the embodiments of the present invention. Unless otherwise indicated, all parts and percentages are on a weight basis.

EXAMPLE 1

The metal substrate employed in this example was an expansion cone comprised of 1.3 mm gauge 309 stainless steel. The expansion cone had a length of 172 mm, an inside diameter ranging from 40.2 mm to 66.4 mm and a calculated area of 0.0288 m². The expansion cone was sandblasted, washed with 30% acetic acid and rinsed with distilled water.

The cleaned expansion cone was then air gun-sprayed with an aluminum-silicate dispersion having the following composition: component amount, wt. % sodium potassium aluminum silicate about 40 to about 45 water about 35 to about 40 acrylic copolymer about 1 to about 5 chromia titania frit about 1 to about 5 aluminum oxide about 1 to about 5 potassium hydroxide about 1 to about 5 amorphous silica about 1 to about 5 cobalt oxide about 1 to about 5

The sprayed expansion cone was then calcined at a temperature of 450° C. for a period of 30 minutes. Laboratory thermal shock testing indicated that the alumina-silicate coating readily survives temperature cycling in excess of 1000° C.

After calcination, the cone was cooled to room temperature and a washcoat comprised of an engine exhaust treatment catalyst was then applied at a target rate of 1.75 g per cone using a hand held air spray gun so as to apply 0.07 g precious metal per cone. The washcoat consisted of an aqueous slurry (35 wt. % solids) of an engine exhaust treatment catalyst consisting of the following components: component amount, g/in³ high surface area alumina 0.61 CeZr coprecipitated composite 0.31 barium acetate 0.04 zirconium acetate 0.025 Pt (as ammonium hydroxide) 0.037 Pd (as nitrate) 0.0037

The resultant cone was then air dried at 80° for 1 hour and then calcined at 450° C. for 30 minutes. No further studies were conducted on the coated expansion cone since the wash coat slurry did not adhere to the surface of the alumina-silicate coated expansion cone.

EXAMPLE 2

Example 1 was repeated with the following exceptions: The expansion cone was coated with the same aluminum-silicate dispersion by means of a sponge roller rather than by air gun spraying. The coated cone was then dipped into alumina powder having a particle size range of 2-15 microns) while the surface of the cone was still wet with the aluminum-silicate dispersion. The cone was then tapped on a hard surface to remove loose alumina particles followed by calcination at a temperature of 450° C. for a period of 30 minutes. The coated cone contained about 0.3 g of the alumina particles.

Following calcination, the cone was cooled to room temperature and the same washcoat as employed in Example 1 was applied to the coated cone at a target rate of 1.75 g per cone using a hand held air spray gun so as to apply 0.07 g precious metal per cone. The resultant cone was then air dried at 80° for 1 hour and then calcined at 450° C. for 30 minutes.

Laboratory thermal shock testing of the coated cone of Example 2 indicated that the alumina-silicate coating readily survives temperature cycling in excess of 1000° C. The coated cone of Example 2 was close-coupled engine aged on a stationary generator for a period of about 300 hours. Visual inspection of the aged cone showed no significant physical deterioration of the coating. 

1. A coated metal substrate for use in the catalytic reduction of engine exhaust emissions comprising a metal substrate having an alumina-silicate coating thereon, said alumina-silicate coating having alumina particles dispersed therein.
 2. The substrate of claim 1 further comprising at least one top layer comprising an engine exhaust treatment catalyst.
 3. The substrate of claim 2 wherein the catalyst comprises a three-way conversion catalyst.
 4. The substrate of claim 1 wherein the metal substrate comprises a metal selected from the group consisting of a stainless steel, a carbon steel, titanium, a FeCr alloy and Hastelloy.
 5. The substrate of claim 4 wherein the metal substrate comprises a stainless steel.
 6. The substrate of claim 1 wherein the alumina particles have a particle size in the range of about 5 to about 15 microns.
 7. The substrate of claim 6 wherein the alumina particles have a particle size in the range of 6 to 9 microns.
 8. The substrate of claim 1 wherein the alumina particles are present in an amount of about 0.1 to about 0.5 g/in² of the alumina-silicate coating.
 9. The substrate of claim 1 wherein the metal substrate is employed in the form of an expansion cone or exhaust gas silencer.
 10. The substrate of claim 9 wherein the expansion cone has a length of about 100 to about 300 mm, a diameter ranging from about 30 to about 100 mm, a thickness of about 0.5 to about 3 mm and an inside surface area of about 0.03 to about 0.06 m².
 11. A method for preparing a coated metal substrate for use in the catalytic reduction of engine exhaust emissions comprising the steps of: (a) coating a metal substrate with a liquid dispersion containing an aluminum silicate; (b) impregnating the coated metal substrate resulting from step (a) with alumina particles, while the aluminum silicate coating on the metal substrate is still wet; and (c) calcining the coated metal substrate resulting from step (b).
 12. The method of claim 11 wherein step (c) is carried out at a temperature of about 350 to about 550° C. for about 0.25 to about 2 hours.
 13. The method of claim 11 further comprising applying a washcoat comprising an engine exhaust treatment catalyst to the coated metal substrate resulting from step (c).
 14. The method of claim 13 wherein the catalyst comprises a three-way conversion catalyst.
 15. The method of claim 11 wherein the metal substrate comprises a metal selected from the group consisting of a stainless steel, a carbon steel, titanium, a FeCr alloy and Hastelloy.
 16. The method of claim 15 wherein the metal substrate comprises a stainless steel.
 17. The method of claim 11 wherein the alumina particles have a particle size in the range of about 5 to about 15 microns.
 18. The method of claim 17 wherein the alumina particles have a particle size in the range of 6 to 9 microns.
 19. The method of claim 11 wherein the alumina particles are present in an amount of about 0.01 to about 0.5 g/in² of the aluminum silicate coating.
 20. The method of claim 11 wherein the metal substrate is employed in the form of an expansion cone or exhaust gas silencer.
 21. The method of claim 19 wherein the expansion cone has a length of about 200 to about 300 mm, a diameter ranging from about 30 to about 100 mm, a thickness of about 0.5 to about 3 mm and an inside surface area of about 0.03 to about 0.06 m².
 22. The method of claim 11 wherein the liquid dispersion comprises the following components in the indicated amounts: component amount, wt. % sodium potassium aluminum silicate about 40 to about 45 water about 35 to about 40 acrylic copolymer about 1 to about 5 chromia titania frit about 1 to about 5 aluminum oxide about 1 to about 5 potassium hydroxide about 1 to about 5 amorphous silica about 1 to about 5 cobalt oxide about 1 to about 5


23. The method of claim 11 wherein the liquid dispersion comprises the following components in the indicated amounts: component amount, wt. % silicon carbide about 45 to about 50 water about 20 to about 26 aluminum phosphate about 10 to about 15 amorphous silicon oxide binders about 2 to about 6 boric acid about 1 to about 3 ethyl alcohol about 3 to about 7 mullite about 4 to about 6 